Abstract

Extensive investigations of the high temperature strength and ductility of a number of platinum and palladium alloys have not yielded a successful replacement for the rhodium-platinum alloys so widely used in applications involving high stress, although they have indicated several alloys with economic possibilities at intermediate temperatures.

Loading

Article metrics loading...

/content/journals/10.1595/003214073X174130136
1973-01-01
2024-06-12
Loading full text...

Full text loading...

/deliver/fulltext/pmr/17/4/pmr0017-0130.html?itemId=/content/journals/10.1595/003214073X174130136&mimeType=html&fmt=ahah

References

  1. Reinacher G. 1Metall, 1958, 12, 622628 [Google Scholar]
  2. Reinacher G. 2Metall, 1961, 15, 657665 [Google Scholar]
  3. Reinacher G. 3Metall, 1962, 16, 662668 [Google Scholar]
  4. Reinacher G. 4Metall, 1971, 25, 740748 [Google Scholar]
  5. Reinacher G. 5Metall, 1973, 27, 659661; see also German Offen. 1,950,468, April 1971 [Google Scholar]
  6. Reinacher G. 6Z. Metallkde., 1962, 53, (7), 444449 [Google Scholar]
  7. Reinacher G. 7Metall, 1972, 26, (7), 673680 [Google Scholar]
  8. Rytvin E. I., Kuz’min V. M., and Petrova A. E. 8Metalloved. Term. Obrabot. Metallov, 1967, 2, 3132 [Google Scholar]
  9. Sadowski E. P. 9“Refractory Metals and Alloys,”Interscience Publishers, New York, London, 1961, p. 465 [Google Scholar]
  10. Aliotta J., and Satterfield E. L. 10U.S. Patent 3,488,172, Owens Corning [Google Scholar]
  11. 11 Johnson Matthey and Co Ltd, unpublished information
  12. 12 Owens Corning, German Offen. 2,154,517, May 1973 [Google Scholar]
/content/journals/10.1595/003214073X174130136
Loading
/content/journals/10.1595/003214073X174130136
Loading

Data & Media loading...

  • Article Type: Research Article
This is a required field
Please enter a valid email address
Approval was a Success
Invalid data
An Error Occurred
Approval was partially successful, following selected items could not be processed due to error