Abstract

The initial phase in the development of a new class of high temperature materials based upon the incorporation of platinum group metals as alloy constituents in nickel based superalloys has been reported here previously. It was shown that the new alloys provide enhanced resistance to environmental corrosion when compared with their conventional base metal counterparts, without detriment to high temperature strength. This paper describes the results of more detailed studies of the constitutional and structural aspects of these complex alloys which led to the design of a developmental alloy, RJM2012, specifically tailored for operation under the aggressive environmental conditions found in the industrial and marine gas turbine.

Loading

Article metrics loading...

/content/journals/10.1595/003214082X264146157
1982-01-01
2024-06-23
Loading full text...

Full text loading...

/deliver/fulltext/pmr/26/4/pmr0026-0146.html?itemId=/content/journals/10.1595/003214082X264146157&mimeType=html&fmt=ahah

References

  1. Corti C. W., Coupland D. R., and Selman G. L. Platinum Metals Rev., 1980, 24, (1), 2 [Google Scholar]
  2. Decker R. F. Proc. Symp. Steel Strengthening Mechanisms, sponsored by Climax Molybdenum Co., Zürich, 5–6th May, 1969, pp. 147170 [Google Scholar]
  3. Beeston B. E. P., and France L. K. J. Inst. Met., 1968, 96, 105 [Google Scholar]
  4. Beeston B. E. P., Dillamore I. L., and Smallman R. E. Met. Sci. J., 1968, 2, 12 [Google Scholar]
  5. Pelloux R. M. N., and Grant N. J. Trans. Met. Soc. AIME, 1960, 218, (4), 232 [Google Scholar]
  6. Parker E. R., and Hazlett T. H. Trans. A. S. M., 1954, 46A, 701 [Google Scholar]
  7. Gleiter H., and Hornbogen E. Phys. Status Solidi, 1965, 12, (1), 235 and 251 [Google Scholar]
  8. Kear B. H., Oblak J. M., and Giamei A. F. Met. Trans., 1970, 1, (9), 2477 [Google Scholar]
  9. Nicholls J. R., and Rawlings R. D. J. Mater. Sci., 1977, 12, (12), 2456 [Google Scholar]
  10. Liang S. J., and Pope D. P. Acta Metall., 1977, 25, (5), 485 [Google Scholar]
  11. Schwarz R. B., and Labusch R. J. Appl. Phys., 1978, 49, (10), 5174 [Google Scholar]
  12. Suzuki K., Ichihara M., and Takeuchi S. Acta Metall., 1979, 27, (2), 193 [Google Scholar]
  13. Suzuki T., Oya Y., and Wee D.-M. Acta Metall., 1980, 28, (3), 301 [Google Scholar]
  14. Suzuki T., and Oya Y. J. Mater. Sci., 1981, 16, (10), 2737 [Google Scholar]
  15. Reppich B. Acta Metall., 1982, 30, (1), 87 [Google Scholar]
  16. Reppich B., Schepp P., and Wehner G. Acta Metall., 1982, 30, (1), 95 [Google Scholar]
  17. Wee D.-M., Noguchi O., Oya Y., and Suzuki T. Trans. Jpn. Inst. Met., 1980, 21, (4), 237 [Google Scholar]
  18. Wee D.-M., and Suzuki T. Trans. Jpn. Inst. Met., 1979, 20, (11), 634 [Google Scholar]
  19. Restall J. E. Proceedings of the 3rd Int. AIME Symposium on Superalloys, Seven Springs, PA, Sept., 1976, pp. 351357 [Google Scholar]
  20. Restall J. E., and Weaver M. J. British Patent1,381,859; 1975 [Google Scholar]
  21. Restall J. E., and Weaver M. J. U.S. Patent 3,922,168; 1975 [Google Scholar]
  22. Pratt A. S., and Coupland D. R. British Patent 2,029,857 B; 1982 [Google Scholar]
  23. Rawlings R. D., and Staton-Bevan A. E. J. Mater. Sci., 1975, 10, (3), 505 [Google Scholar]
  24. Kriege O. H., and Baris J. M. Trans. A.S.M., 1969, 62, (1), 195 [Google Scholar]
  25. Donachie M. J., and Kriege O. H. J. Mater., 1972, 7, (3), 269 [Google Scholar]
  26. Wing R. G., and McGill I. R. Platinum Metals Rev., 1981, 25, (3), 94 [Google Scholar]
/content/journals/10.1595/003214082X264146157
Loading
/content/journals/10.1595/003214082X264146157
Loading

Data & Media loading...

  • Article Type: Research Article
This is a required field
Please enter a valid email address
Approval was a Success
Invalid data
An Error Occurred
Approval was partially successful, following selected items could not be processed due to error